Product Description

Artificial Graphite HC15 for Power Lithium Battery


Category:

Artificial graphite


Advantages:

High energy density

Long battery life

1.5C charging rate


Application:

Artificial Graphite HC15 is widely used to Power Lithium batteries. Power lithium battery has the advantages of high energy, high battery voltage, wide operating temperature range, long storage life and so on. It has been widely used in military and civil small electrical vehicle (EV) batteries or large capacity and power batteries in other applicaitosn, partly replacing the traditional battery.


Tips:

The material design first discharge capacity is recommended to be 350mAh/g, and the tap density is recommended to be controlled in 1.60g/cc and below. This product is suitable for aqueous solution lithium battery system.


Packaging requirements:

HC15 artificial graphite shall be packed into a plastic bag with a specification of 650mm×950mm, sealed and then placed into a carton with a weight of 25+0.02kg/ box, or according to customer requirements packaging.


Transportation and storage:

a. The product should be stored in a place where dry, ventilated and no other pollution sources (recommended: temperature ≤ 45 ° C, humidity ≤85%);

b. Product stacking should be neat, clean, production lot number, production date, etc. should be clearly identified;

c. During the transportation process, it should be gently put, so as not to damage the packaging; Any products leaking out of the bag shall not be returned to the box.

d. The shelf life is 2 years in a normal temperature state.


Packaging and product identification:

H5 product packaging must be marked with the following information:

A) Product Name

B) Batch Number of product

C) Product weight

D) Date

E) Company Name


Matters needing attention:

A) Ensure that the capacity of the negative electrode per unit area is greater than or equal to that of the positive electrode per unit area to avoid lithium evolution during charging.

B) Ensure that there is a good interface between the isolation film and the electrode.

C) The surface density and compaction density of the electrode will affect the performance of the rate capacity and performance.

D) The product is of secondary particle + single particle structure, and it is recommended that the design pressure below 1.55-1.60g/cc is the best.





    Technical indicators:


    Number

    Name

    Unit

    Standard

    Typical values

     

     

     

    1

     

     

     

    Particle size

    Dmin

    um

    ≥1.5

    1.78

    D10

    um

    6.0±2.0

    6.34

    D50

    um

    14.0±2.0

    13.97

    D90

    um

    24.0±3.0

    24.54

    Dmax

    um

    ≤55

    45.19

    2

    TAP

    g/cc

    1.0±0.1

    1.03

    3

    SSA

    m2/g

    1.0-2.0

    1.50

    4

    C

    %

    ≥99.95

    99.985

     

    5

    Tap Density

    g/cc

    1.60-1.63

    ~1.60

    First discharge capacity

    mAh/g

    ≥352

    354.4

    6

    True Density

    g/cc

    ≥2.20

    2.27

    7

    First discharge capacity

    %

    ≥92%

    95.4

     

     

     

    8

     

     

     

    Trace   elements

    Fe

    ppm

    ≤15

    7.98

    Co

    ppm

    ≤5

    0.34

    Cu

    ppm

    ≤5

    --

    Ni

    ppm

    ≤5

    0.12

    Al

    ppm

    ≤5

    --


    Particle Size Distribution:

    1646378914311044.png


    Discharge Capacity:

    HC15 mahg.png

    XRD:

    HC15 XRD.png